Effect of Thermomechanical Treatment Temperature on Structure and Properties of CFB/M Ultra-High Strength Steel 被引量:3

Effect of Thermomechanical Treatment Temperature on Structure and Properties of CFB/M Ultra-High Strength Steel
原文传递
导出
摘要 Modified CCT diagram of carbide-flee bainite-martensite (CFB/M) ultra-high strength steel was established by applying controlled cooling of small samples. In addition, the influence of thermomechanical treatment tem- perature on the structure and properties was discussed. The experimental results showed that when deformed at 860℃ and below, ferrite transformation occurred due to strain. With the decrease of ausforming temperature, the quantity of ferrite increased and strength and toughness were deteriorated. Therefore, certain information was provided for optimizing technical parameter of ausforming process., firstly, the thermomechanical treatment temperature should not be lower than 860 ℃ in order to avoid ferrite formation induced by deformation; secondly, rapid cooling rate is also significant after deformation in order to avoid ferrite precipitation during subsequent cooling stage. Modified CCT diagram of carbide-flee bainite-martensite (CFB/M) ultra-high strength steel was established by applying controlled cooling of small samples. In addition, the influence of thermomechanical treatment tem- perature on the structure and properties was discussed. The experimental results showed that when deformed at 860℃ and below, ferrite transformation occurred due to strain. With the decrease of ausforming temperature, the quantity of ferrite increased and strength and toughness were deteriorated. Therefore, certain information was provided for optimizing technical parameter of ausforming process., firstly, the thermomechanical treatment temperature should not be lower than 860 ℃ in order to avoid ferrite formation induced by deformation; secondly, rapid cooling rate is also significant after deformation in order to avoid ferrite precipitation during subsequent cooling stage.
出处 《Journal of Iron and Steel Research(International)》 SCIE EI CAS CSCD 2010年第4期66-72,共7页 钢铁研究学报(英文版)
基金 Item Sponsored by National Key Fundamental Research and Development Programme of China(2004CB619105)
关键词 thermomechanical treatment carbide-free bainite/martensite (CFB/M) ultra-high strength steel thermomechanical treatment carbide-free bainite/martensite (CFB/M) ultra-high strength steel
  • 相关文献

参考文献5

二级参考文献35

共引文献147

同被引文献25

  • 1袁书强,沈正祥,周春华,刘峰涛,王芳,杨辉,陈炯.不同热处理条件下30CrMnSiNi2A钢的组织性能研究[J].材料科学与工艺,2015,23(2):125-128. 被引量:10
  • 2张旺峰,朱金华,曹春晓.奥氏体锰钢高应变速率孪生诱导塑性[J].机械工程材料,2005,29(3):14-17. 被引量:3
  • 3李相波,王佳,郭为民,王伟.微生物附着对不锈钢钝化性能的影响[J].中国腐蚀与防护学报,2006,26(5):295-298. 被引量:5
  • 4刘建涛,张义文,陶宇,刘国权,胡本芙.FGH96合金动态再结晶行为的研究[J].材料热处理学报,2006,27(5):46-50. 被引量:36
  • 5Kenichiro Moil, Yohei Abe,Yoshio Suzui. Improvement of stretch flangeability of ultra high strength steel sheet by smoothing of sheared edge [ J ]. Journal of Materials Processing Technology,2010,210 (4) :653 - 659.
  • 6Mori K,Akita K, Abe Y. Springback behaviour in bending of ultra-high-strength steel sheets using CNC servo press [ J ]. International Journal of Machine Tools and Manufacture,2007,47 (2) :321 - 325.
  • 7ZOU Ji-quan, JING Hong-yang, XU Lian-yong. Surface crack fracture toughness and HRR fields of ultra-high strength steel [ J ]. Materials Science and Engineering A ,2007,454 - 455:467 - 471.
  • 8Mori K, Saito S, Maki S. Warm and hot punching of ultra high strength steel sheet[J]. CIRP Annals-Manufacturing Technology,2005,57 (1) :321 - 324.
  • 9Frommert M, Gottstein G. Mechanical behavior and microstructure evolution during steady-state dynamic recrystallization in the austenitie steel 800H [ J ]. Materials Science and Engineering A ,2009,506 ( 1 - 2 ) : 101 - 110.
  • 10张江涛,吴龙益.机载设备霉菌防护设计[J].装备环境工程,2007,4(6):70-73. 被引量:9

引证文献3

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部