7050铝合金板在固溶过程中微结构与织构的演变 被引量:29

Evolutions of microstructures and textures of 7050 Al alloy plate during solution heat treatment
下载PDF
导出
摘要 采用光学金相(OM)、扫描电镜(SEM)、透射电镜(TEM)、X射线衍射(XRD)和织构材料(ODF)分析等研究7050铝合金热轧板在逐级升温固溶过程中微结构与织构的演变。结果表明:在固溶温度不超过490℃的条件下,板材中长条形再结晶晶粒平行于轧向分布,固溶板材与热轧板材的织构组态相似,均含有少量{001}<100>织构,晶粒取向主要聚集在β-取向线和α-取向线上;具有{124}<211>和{112}<111>取向的形变长条形组织由于回复和连续再结晶使其取向逐渐趋同,取向密度增强;最后经(475℃,12h)处理的样品中残留有Al2CuMg和Al7Cu2Fe相;而经(490℃,4h)处理的样品中,Al2CuMg相全部溶入基体,Al7Cu2Fe相仍然存在。 Evolutions of microstructures and textures of 7050 Al alloy hot rolled plate during solution heat treatment were studied by OM,SEM,TEM,XRD and ODF techniques.The results show that when the samples are heated stage by stage up to 490 ℃,the lamellar grains are still parallel to the rolling direction.The textures of the solution treated samples are similar to the rolled ones.The grain orientations mainly concentrate to β-fiber and α-fiber,in company with a little {001}〈100〉 texture.The orientations densities of {124}〈211〉 and {112}〈111〉 textures increase with the recovery and continuous recrystallization of the deformed lamellar matrix.The sample,which is held at 475 ℃ for 12 h in the last stage during the solution,contains Al2CuMg and Al7Cu2Fe particles.The sample,which is held at 490 ℃ for 4 h in the last stage during the solution,still includes Al7Cu2Fe particles,but excludes Al2CuMg particles.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2010年第3期427-434,共8页 The Chinese Journal of Nonferrous Metals
基金 国家重点基础研究发展计划资助项目(2005CB623700) 中铝公司基金资助项目(CHALCO-2007-KJ-07)
关键词 7050铝合金 固溶 微结构 织构 再结晶 7050 Al alloy solution microstructure texture recrystallization
  • 相关文献

参考文献15

  • 1HEINZA A,HASZLER A,KEIDEL C,MOLDENHAUER S,BENEDICTUS R.Recent development in aluminium alloys for aerospace applications[J].Mater Sci Eng A,2000,280:102-107.
  • 2冯春,刘志义,宁爱林,曾苏民.RRA处理对超高强铝合金抗应力腐蚀性能的影响[J].中南大学学报(自然科学版),2006,37(6):1054-1059. 被引量:24
  • 3DUMONT D,DESCHAMPS A,BRECHET Y.Characterisation of precipitation microstructures in aluminium alloys 7040 and 7050 and their relationship to mechanical behavior[J].Acta Materialia,2003,51(3):713-729.
  • 4WANG D,NI D R,MA Z Y.Effect of pre-strain and two-step aging on microstructure and stress corrosion cracking of 7050 alloy[J].Mater Sci Eng A,2008,494:360-366.
  • 5WANG D,MA Z Y.Effect of pre-strain on microstructure and stress corrosion cracking of over-aged 7050 aluminum alloy[J].Journal of Alloys and Compounds,2009,469:445-450.
  • 6田福泉,崔建忠.双级时效对7050铝合金组织和性能的影响[J].中国有色金属学报,2006,16(6):958-963. 被引量:53
  • 7CAI B,ADAMS B L,NELSON T W.Relation between precipitate-free zone width and grain boundary type in 7075-T7 Al alloy[J].Acta Mater,2007,55(10):1543-1553.
  • 8LIU S D,ZHANG X M,CHEN M A,YOU J H.Influence of aging on quench sensitivity effect of 7055 aluminum alloy[J].Mater Char,2008,59:53-60.
  • 9LI Xiao-mei,STARINK M J.The effect of compositional variations on the characteristics of coarse intermetallic particles in overaged 7xxx Al alloys[J].Mater Sci Technol,2001,17:1324-1328.
  • 10LI Xiao-mei,STARINK M J.Analysis of precipitation and dissolution in overaged aluminum alloys using DSC[J].Mater Sci Forum,2000,331/337:1071-1076.

二级参考文献49

共引文献105

同被引文献237

引证文献29

二级引证文献187

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部