摘要
钢铁防腐涂层的施工中经常发现因各种不同原因引起的涂层起泡现象,因此,造成了涂层缩孔、针孔、鱼眼等不同的涂层弊病。泡的存在严重影响了涂层的保护效果、外观检验。本文分析了起泡产生的不同原因和容易引起的各种涂层缺陷,对确定防腐涂层的修补方案具有指导意义。
coating defects blistering on steel such as craterings, influenced by blistering. Analyze surface coating frequently occurs during paint application, it will bring pin-holes, fish eyes etc. The coating function and appearance was greatly what caused the blistering was needed on coating repairs.
出处
《全面腐蚀控制》
2010年第4期41-43,共3页
Total Corrosion Control
关键词
涂层缺陷
原因
控制
coating defects
reason
control