摘要
用熔融玻璃净化与循环过热相结合的方法,研究了BFe30-2合金过冷熔体凝固组织的演化规律。研究表明:在过冷度39~203K的范围内,其凝固组织的形态有三次变化过程:第一次是在39~118K过冷度范围,随着过冷度的增加,凝固组织中枝晶明显细化且同时存在枝晶重熔形成的第一类粒状晶;第二次发生在118~174K过冷度范围,因枝晶熟化被抑制,形成的第一类粒状晶转变为高度细化的细枝晶;第三次发生在174~203K过冷度区间,组织因细枝晶再结晶转变为均匀的准球状晶粒。
The microstructure evolution of undercooled melt of BFe30-2 alloy was investigated by means of melted glass purification and cyclical superheating.The results indicate that,within the undercooling range(39 ~203 K),the microstructure undergoes three transformation processes.Within the first procedure of undercooling range(39~118 K),the coarser dendrites become fine clearly and the first granular is formed by dendrites remelting with the increase of undercoling.Within the second procedure of undercooling range(118~174 K),the first granular changes into highly finer dendrites due to the restrained ripening course.Within the third procedure of undercooling range(174~203 K),a kind of even quasi-spherical grain is formed by the recrystallization of highly finer dendrites.
出处
《热加工工艺》
CSCD
北大核心
2010年第7期9-11,共3页
Hot Working Technology
基金
宁夏自然科学基金(NZ0843)
山西省高校科技研究开发项目(20063027)
关键词
过冷
BFe30-2合金
凝固组织
演化
undercooling
BFe30-2 alloy
solidification microstructure
evolution