摘要
通过加热实验、轧制实验、冷却实验及温度场模拟的研究,分析线材表面氧化铁皮与各影响因素间的对应关系,进而改进生产工艺,使帘线钢表面氧化层平均厚度减小52%左右,稳定在6.0μm左右,最大厚度≤10.0μm,取得良好的效果.
Heating, roiling and cooling experiments, as well as temperature field simulation were undertaken to analyze the figure out the relations of the surface oxide scale formation with a number of influencing factors, and then to improve the production processes. As a result, the average thickness of the scale was decreased by about 52 %, reaching an average thickness of 6. 0 μm and a maximum one ≤ 10.0 μm
出处
《南方金属》
CAS
2010年第1期34-37,共4页
Southern Metals
关键词
帘线钢盘条
氧化铁皮
温度场
轧制
cord steel wire rod
iron oxide scale
temperature field
rolling