A lead（II） coordination polymer,{[Pb2（butca）（H2O）2]（H2O）2}n （1）,has been synthe-sized by the hydrothermal reaction of Pb（OH）2 and 1,2,3,4-butanetetracarboxylic acid （H4butca） at 160 °C.Single-crystal X-ray analyses reveal that it crystallizes in monoclinic,space group P21/c with a=7.616（5）,b=7.584（4）,c=12.314（7）,β=105.595（12）o,V=685.0（7）3,Z=4,C8H14O12Pb2,Mr=716.57,Dc=3.474 g/cm3,μ=24.610 mm-1,F（000）=644,the final R=0.0381 and wR=0.1176 for 1465 observed reflections with I 〉 2σ（I）.The complex presents a 2D-layered structure featuring two different types of rings,and has a （4,36）topology based on Pb and butca4-nodes.In solid state,complex 1 shows photoluminescence with the maximum emission intensity at 468 nm under 286 nm excitation.
A lead（II） coordination polymer,{[Pb2（butca）（H2O）2]（H2O）2}n （1）,has been synthe-sized by the hydrothermal reaction of Pb（OH）2 and 1,2,3,4-butanetetracarboxylic acid （H4butca） at 160 °C.Single-crystal X-ray analyses reveal that it crystallizes in monoclinic,space group P21/c with a=7.616（5）,b=7.584（4）,c=12.314（7）,β=105.595（12）o,V=685.0（7）3,Z=4,C8H14O12Pb2,Mr=716.57,Dc=3.474 g/cm3,μ=24.610 mm-1,F（000）=644,the final R=0.0381 and wR=0.1176 for 1465 observed reflections with I 〉 2σ（I）.The complex presents a 2D-layered structure featuring two different types of rings,and has a （4,36）topology based on Pb and butca4-nodes.In solid state,complex 1 shows photoluminescence with the maximum emission intensity at 468 nm under 286 nm excitation.
基金
Supported by the Education Department of Jiangxi Province (No. 2007-125)
the Initial Fund for Doctors from Jiangxi Normal University