为了得到一种理想的水凝胶伤口敷料,研究了应用电子束辐射接枝了不同比例聚乙烯醇(PVA)的聚氧化乙烯(PEO)水凝胶膜的制备和该膜的理化特性。实验结果显示,PEO接枝水凝胶膜的凝胶分数主要依赖于辐射剂量和聚合物浓度。而其溶胀度与辐射剂量聚合物的浓度;混合比例和分子量密切相关。该膜的抗张强度和断裂伸长率则明显地依赖于辐射剂量和聚合物的混合比例。实验发现,比例为7:3的20wt%PEOE-30接枝水凝胶膜与其它PEO接枝水凝胶膜和单纯PEOE-30水凝胶膜相比具有较好的理化特性,例如韧性,较少气泡,适度的凝胶分数,溶胀度和断裂伸长率,尤其它的较高的抗张强度。实验结果表明,PVA在辐射接枝后能够通过降低PEO水凝胶膜的溶胀度而改善PEO水凝胶膜的机械强度。
In order to obtain a more ideal hydrogel wound dressing, PEO graft hydrogel films formed by electron beam(EB) irradiation of the aqueous solutions of poly(ethylene oxide)(PEO) incorporated with poly(vinyl alcohol) (PVA) at different ratio were prepared, and their physiochemical properties were investigated as a function of production factors combination. The experimental results showed that gel fraction of the PEO graft hydrogel films depended mainly on irradiation dose and concentration of the polymers. Their degree of swelling was intimately elated to irradiation dose, concentration, bledding ratio and molecular weight of the polymers. Their tensile strength and elongation at break were obviously dependent on irradiation dose and blending ratio of the polymers. It is found that a new PEO E-30 graft hydrogel film of 20 wt% at a ratio of 7:3 has better physiochemical properties such as fiekibility, moderate gel fraction, degree of swelling and elongation at break, especially its higher tensile strength than other PEO graft hydrogel films or pure PEO E-30 hydrogel film. These results indicated that PVA can improve the mechanical strength of the PEO E-30 hydrogel film through reducing the degree of swelling of the PEO E-30 hydrogel film after the irradiation graft.
出处
《辐射研究与辐射工艺学报》
CAS
CSCD
北大核心
1999年第1期9-14,共6页
Journal of Radiation Research and Radiation Processing
基金
中日双边科技合作项目
中国核工业科学研究基金
关键词
聚氧化乙烯
聚乙烯醇
水凝胶膜
辐射接枝
Poly(ethylene oxide), Poly(vinyl alcohol), Hydrogel, Property, Radiation graft