SAE8620H钢奥氏体连续冷却转变曲线 被引量:7

Austenite continuous cooling transformation curve of SAE8620H steel
下载PDF
导出
摘要 采用Formastor-digital全自动相变测量仪,测定SAE8620H钢的临界点Ac1,Ac3,Ar3,Ar1以及不同冷却速度下连续冷却时的膨胀曲线,研究冷却速度对组织及硬度的影响。结果表明:当冷却速度为50℃/h,转变产物为先共析铁素体、珠光体和少量的3次渗碳体;当冷速为3 200℃/h时,转变产物为先共析铁素体、珠光体组织和贝氏体组织;冷速为120~600℃/min时,转变产物基本上是贝氏体组织;临界淬火冷却速度大于60℃/s可得到完全马氏体组织。 By Formastor-digital automatic phase transformation instrument,the critical point Ac1,Ac3,Ar3 and Ar1 of SAE8620H steel were determined.By measuring,the different CCT diagram was obtained.The influence of cooling rate on steel microstructure and hardness was studied.The results show that when the cooling rate is 50 ℃/h,the products of austenite transformation will be ferrite,pearlite and cementite;when the cooling rate is 3 200 ℃/h,the products will be ferrite,pearlite and bainite;when the cooling rate is in the range of 120-600 ℃/min,the products will be bainite and totally martensite if the cooling rate is higher than 60 ℃/s.
出处 《兵器材料科学与工程》 CAS CSCD 2010年第3期85-87,共3页 Ordnance Material Science and Engineering
关键词 SAE8620H钢 热膨胀法 过冷奥氏体 CCT曲线 SAE8620H steel thermal dilation method undercooling austenite continuous cooling transformation curve
  • 相关文献

参考文献4

  • 1YB/5127-1993,钢的临界点测定方法(膨胀法)[S].
  • 2YB/5128-1993,钢的连续冷却转变曲线图的测定方法:膨胀法[S].
  • 3崔忠圻.金属学与热处理[M].北京:机械工业出版社,2006.240-244
  • 4冶金工业部钢铁研究总院.合金钢手册上册[M].北京:冶金工业出版社.1984:490.

共引文献10

同被引文献32

引证文献7

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部