采用表面熔渗技术在AZ91D镁合金浇注过程中同步形成了富Al表面熔渗层,并对熔渗层的厚度、微观组织和微区成分进行了分析。结果表明,镁合金表面富Al熔渗层与基体组织为冶金结合;随模具表面Al粉涂敷层厚度的增加,镁合金表面熔渗层逐渐变得连续、致密,且厚度也不断增加,但对各微区化学成分影响较小;镁合金表面熔渗层中Al含量从表面向内部逐渐降低。
Rich Al infiltration layer on AZ91 D magnesium alloy surface was prepared synchronously in die casting process by surface infiltration technology. Thickness,microstructure and micro-area composition in the infiltration layer were analyzed. The results show that the rich Al infiltration layer exhibits metallurgical bonding with the matrix. With increasing in thickness of coated Al powder on surface of mould,infiltration layer on the magnesium alloy surface becomes continuous and compact with thickness increase,however,change of chemical composition in micro-area shows slightly. Al content in infiltration layer is decreased gradually from surface to inner layer.
出处
《特种铸造及有色合金》
CAS
CSCD
北大核心
2010年第6期564-565,共2页
Special Casting & Nonferrous Alloys
基金
辽宁省政府镁资源基金资助项目(990068-2007)
关键词
镁合金
Al粉
表面
熔渗
Magnesium Alloy,Aluminum Powder,Surface,Infiltration