摘要
The effects of the composition and cooling process on the microstructures and properties of hot-rolled ultra-high strength low alloy （HSLA） steel, complex phase steel and martensite steel were studied in the laboratory. And S700MC and MP1200 ultra-high strength steels were trial produced at the 1 880 mm hot-rolling line of Baosteel. Compared with conventional hot-rolled high strength products,the idea that water is alloy was applied in the newly developed hot-rolled ultra-high strength steel. By the use of the economical composition design and controlled cooling after hot-rolling effectively,ultra-high strength steel of different steel grades can be obtained.
The effects of the composition and cooling process on the microstructures and properties of hot-rolled ultra-high strength low alloy （HSLA） steel, complex phase steel and martensite steel were studied in the laboratory. And S700MC and MP1200 ultra-high strength steels were trial produced at the 1 880 mm hot-rolling line of Baosteel. Compared with conventional hot-rolled high strength products,the idea that water is alloy was applied in the newly developed hot-rolled ultra-high strength steel. By the use of the economical composition design and controlled cooling after hot-rolling effectively,ultra-high strength steel of different steel grades can be obtained.