ZnO whiskers with a length of 30-40μm and a diameter of about 1μm were synthesized by co-precipitation of ZnSO 4 and Na2CO3 solution at room temperature followed by hydrothermal treatment of the as-prepared Zn5(CO3)2(OH)6 precursor at 160 ℃for 6 h.The increase of the initial solution pH promotes the hydrothermal conversion of the particulate Zn5(CO3)2(OH)6 to ZnO whiskers.The presence of minor amount of EDTA in the hydrothermal solution promotes the one dimensional growth of ZnO whiskers,leading to the formation of ZnO whiskers with a length of 50-60μm and a diameter of 1-2μm.
ZnO whiskers with a length of 30-40μm and a diameter of about 1μm were synthesized by co-precipitation of ZnSO 4 and Na2CO3 solution at room temperature followed by hydrothermal treatment of the as-prepared Zn5（CO3）2（OH）6 precursor at 160 ℃for 6 h.The increase of the initial solution pH promotes the hydrothermal conversion of the particulate Zn5（CO3）2（OH）6 to ZnO whiskers.The presence of minor amount of EDTA in the hydrothermal solution promotes the one dimensional growth of ZnO whiskers,leading to the formation of ZnO whiskers with a length of 50-60μm and a diameter of 1-2μm.
基金
Project(50874066) supported by the National Natural Science Foundation of China