放电等离子体烧结(SPS)制备多晶La_(0.4)Pr_(0.6)B_6块体及其发射性能研究 被引量:5

Fabrication and Emission Property of Polycrystalline La_(0.4)Pr_(0.6)B_6 Bulk Prepared by Spark Plasma Sintering
下载PDF
导出
摘要 采用氢直流电弧法制备了LaH2和PrH2粉末,然后利用放电等离子体烧结(SPS)技术制备了多晶的La0.4Pr0.6B6致密块体.系统分析了烧结温度对样品微观结构及性能的影响,研究结果表明:烧结温度高于1350℃时可形成La0.4Pr0.6B6纯相,且样品致密度随着烧结温度的升高而增加.所制备材料的密度、维氏硬度和抗弯强度的最大值分别达到4.82g/cm3、19.14GPa和225.13MPa;测试了40MPa、1400℃烧结样品的热电子发射性能,当阴极温度为1873K时最大发射电流密度为30.65A/cm2;利用Richardson直线法求出了所测试样品绝对零度时的逸出功φ0为2.165eV,并计算出了样品在不同加热温度时的有效逸出功φeff,其平均值为2.84eV。 The LaH2 and PrH2 nanopowders were prepared by hydrogen arc plasma method,and then dense single-phase polycrystalline La0.4Pr0.6B6 bulks were reactively fabricated starting from mixture of synthesized LaH2,PrH2 nanopowders and boron powders by spark plasma sintering(SPS).The influence of SPS sintering temperature on the microstructure and properties was investigated.Thermionic emission measurement of the sample sintered at 1400℃ and 40MPa was performed.It is shown that the pure phase La0.4Pr0.6B6 bulk can be easily fabricated by SPS when the sintering temperature is higher than 1350℃ and the density of the material increases with increasing temperature.The largest values of densities,Vickers hardness and bend strengths reach 4.82g/cm^3,19.14GPa and 225.13MPa,respectively.The largest emission current density of the cathode heated at 1873K is 30.65A/cm^2.The work function at absolute zero is calculated to be 2.165eV by Richardson line method,and then the average value of effective work functions of the cathode at different temperatures are calculated to be 2.84eV.
出处 《无机材料学报》 SCIE EI CAS CSCD 北大核心 2010年第7期743-747,共5页 Journal of Inorganic Materials
基金 教育部创新工程重大项目培育基金(705004)
关键词 放电等离子体烧结(SPS) 多晶La0.4Pr0.6B6 热发射性能 有效逸出功φeff spark plasma sintering(SPS) polycrystalline La0.4Pr0.6B6 thermionic emission property effective work function
  • 相关文献

参考文献16

  • 1Lafferty J M. Boride cathodes. J.Appl. Phys., 1951, 22(3): 299-302.
  • 2Tanaka T, Nishitani R, Oshima C, et al. The preparation and properties of CeB6, SmB6 and GdB6. J. Appl. Phys., 1980, 51(7): 3877-3883.
  • 3Pademo Y, Pademo V, Filippov V. Some crystal chemistry relationships in eutectic cocrystallization of d- and f-transition metal borides. J. Alloys Compd., 1995, 219(1/2): 116-118.
  • 4Otani S, Aizawa T, Yajima Y, et al. Floating zone growth of LaB6 crystals from the CaB6-added feed rods. J. Cryst. Growth, 2002, 234(2/3): 431-434.
  • 5Bai Lina, Ma Ning, Liu Fengli. Structure and chemical bond characteristics of LAB6. Physica B, 2009, 404(21): 4086-4089.
  • 6周身林,张久兴,刘丹敏,包黎红.放电等离子反应液相烧结制备CeB_6阴极与性能研究[J].无机材料学报,2009,24(4):793-797. 被引量:14
  • 7Goebel Dan M, Watkins Ron M, Jameson Kristina K. LaB6 hollow cathodes for ion and hall thrusters. J. Propul. Power, 2007, 23(3): 552-558.
  • 8Choi Y W, Cho C, Choi Y S, et al. Development of a 30-kW plasma gun system with a long lifetime. IEEE Trans. Plasma Sci., 2008, 36(5): 2765-2769.
  • 9柳术平,杨庆山,陈卫平,刘甲祥,李中华.多元稀土硼化物(La_(0.55)Ba_(0.45))B_6与(La_(0.4)Eu_(0.6))B_6阴极材料的研制[J].稀有金属与硬质合金,2006,34(3):8-11. 被引量:6
  • 10周身林,刘丹敏,张久兴.高纯多晶LaB_6纳米块体阴极材料的制备及表征[J].无机材料学报,2008,23(6):1199-1204. 被引量:11

二级参考文献56

  • 1张粹伟.六硼化镧阴极[J].光电子技术,1989,9(3):35-44. 被引量:5
  • 2张强基.六硼化镧阴极的失效分析[J].电子学报,1989,17(5):115-117. 被引量:4
  • 3陆家和 陈长彦.现代分析技术[M].北京:清华大学出版社,1991..
  • 4A A阿夫琴科.六硼化镧阴极的中毒[J].技术物理杂志(俄),1976,46(10).
  • 5Nishitani T, Aono M, Tanaka T, et al. Surf. Sci., 1980, 95 (2-3): 341-342.
  • 6Futamoto M, Nakazawa M, Kawabe U. Surf. Sci., 1980, 100 (3): 470-471.
  • 7Lafferty J M. J. Appl. Phys., 1951, 22: 299-302.
  • 8Waldhauser W, Mitterer C, Laimer J, et al. Surface and Coatings Technology, 1995, 74-75 (2): 890-896.
  • 9Mushiaki M, Akaishi K, Mori T. Mater. Sci. Eng. A, 1993, 163 (2): 177- 179.
  • 10Nakamoto M, Fukuda K. Appl. Surf. Sci., 2002, 202 (3-4): 289- 294.

共引文献65

同被引文献25

引证文献5

二级引证文献14

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部