采用预裂纹双悬臂梁(DCB)试样研究了7075铝合金的应力腐蚀行为。结果表明,四种不同热处理状态合金的应力腐蚀敏感性由高向低的排列顺序为T6>G180>RRA>T7351。不同热处理状态的7075铝合金试样在干燥空气中的SSRT拉伸断口形貌都是由韧窝剪切台阶组成,属于韧窝型延性断裂。在3.5%NaCl溶液中,应力腐蚀敏感性较高的T6状态铝合金,其断口形貌是由塑性韧窝和腐蚀平坦区组成的,而应力腐蚀敏感性较轻微的7075-G180铝合金,属韧性断裂。
The stress corrosion behavior of 7075 aluminum alloy in different tempers was studied using double cantilever beam（DCB） specimens.The results show that the stress corrosion susceptibility of 7075 aluminum alloy decreases according to the sequence of temper T6 G180 RRA T7351.In dry air,SEM observation of the fracture surface of 7075 alloys in different temper conditions was performed and it is found the ductile fracture pattern composed of dimples and tearing ridge prevails.However,in 3.5% NaCl solution,the fracture of 7075-T6 alloy with high stress corrosion susceptibility exhibits the characteristics of flat corrosion zones and ductile dimples,but the fracture pattern of 7075-G180 alloy with moderate stress corrosion susceptibility presents ductile fracture.
出处
《材料热处理学报》
EI
CAS
CSCD
北大核心
2010年第7期109-113,共5页
Transactions of Materials and Heat Treatment
关键词
热处理
7075铝合金
应力腐蚀
heat treatment
7075 aluminum alloy
stress corrosion