摘要
Co nanostructure tetradecahedron shape like were prepared via a simple solvothermal route. The shape and size of Co nanopolyhedron were tuned by changing the volume composition of the solvents and the synthesis temperature. Phase purity was confirmed by X-ray diffraction （XRD） and crystal size was determined by scanning electron microscopy （SEM）. The magnetic hysteresis loops of the polyhedron wareneasured using a SQUID magnetometer at 5 and 300 K. The results show ferromagnetic characteristics with coercivities of 22 and 15 Oe, respectively.
Co nanostructure tetradecahedron shape like were prepared via a simple solvothermal route. The shape and size of Co nanopolyhedron were tuned by changing the volume composition of the solvents and the synthesis temperature. Phase purity was confirmed by X-ray diffraction （XRD） and crystal size was determined by scanning electron microscopy （SEM）. The magnetic hysteresis loops of the polyhedron wareneasured using a SQUID magnetometer at 5 and 300 K. The results show ferromagnetic characteristics with coercivities of 22 and 15 Oe, respectively.