多次辐照条件下YAG脉冲激光熔敷层开裂敏感性研究 被引量:1

Study of Cracking Sensitivity of Clad Layers Induced by Multi irradiation of a YAG-pulsed Laser
原文传递
导出
摘要 采用Nd:YAG固体脉冲激光器,在镍基高温合金上激光熔敷镍基自熔合金,对激光多次辐照条件下熔敷层的开裂问题进行了探索性研究。试验结果表明:脉冲激光多次辐照,对熔敷层的组织及硬度影响不大;激光辐照次数的增多,促进了熔敷层裂纹萌生,其裂纹形态为沿晶高温液化裂纹;对基材热输入的增多。 The influence of irradiation manner of a YAG pulsed laser on the microstructure and cracking behavior of claddings was characterized. It follows that the microstructures of the cladding may not show a visible change after multi irradiation with the YAG pulsed laser beam, however, multi irradiation do promote the appearance of cracking on claddings. The tendency of cracking of the same cladding may increase with the increase of the number of irradiation. The formed cracks show a feature of along grain boundary like hot cracking. Additionally, more heat input during the process may increase the tendency of initiation of the re heat cracking in the substrate alloy as well.
出处 《中国激光》 EI CAS CSCD 北大核心 1999年第4期363-366,共4页 Chinese Journal of Lasers
关键词 脉冲激光 多次辐照 熔敷 开裂 激光热处理 pulse laser, multi irradiation, cladding, cracking
  • 相关文献

参考文献5

  • 1张松,康煜平,朱荆璞,张春华,谭朝鑫.鼓风机叶片激光熔覆的应用研究[J].中国激光,1995,22(5):395-400. 被引量:15
  • 2Liu Jiafu,Aviation Product Engineering,1993年,10卷,32页
  • 3Wu Weitao,CN 92106197.8,1993年,11页
  • 4J Singh,Metall Trans A,1988年,19卷,8期,1981页
  • 5Zhou Zhenfeng,Weld Metallurgical & Metal Weldability(in Chinese),1988年,203,248页

二级参考文献4

共引文献14

同被引文献10

引证文献1

二级引证文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部