摘要
对正火回火状态的中温临氢钢12Cr2Mo1R进行模拟最小程度焊后热处理试验,采用阶梯冷却加速脆化法,进行了回火脆化处理,并对12Cr2Mo1R钢的回火脆化敏感性进行了研究。试验研究结果表明:12Cr2Mo1R具有良好的抗回火脆化性能,该钢在阶梯冷却试验前后的组织形貌无明显变化。
Steps cooling acceleration embrittlement method was adopted to investigate the temper brittleness of middle temperature hydrogen exposure steel 12Cr2Mo1R. The results show that 12Cr2Mo1R has a good temper brittleness resistance performance and the morphology of steel have no significant changes after steps cooling test.
出处
《钢铁研究》
CAS
2010年第4期16-19,共4页
Research on Iron and Steel
关键词
12CR2MO1R
阶梯冷却
回火脆性
中温临氢钢
12Cr2Mo1R
steps cooling
temper brittleness
middle temperature hydro- gen exposure steel