Uniform ofAgLnMo2O8(Ln=La, Nd, Eu) hierarchical architectures were firstly synthesized via a facile hydrothermal method. These three dimensional architectures were assembled from primary micro-rods and the average diameter was about 5 μm. According to the time-depend experiments, a possible growth mechanism was proposed to be a self-assembling process followed by an Ostwald ripening step. The concentrations of precursor and pH value were also found to have great influences on the final morphologies of the products. In addition, the photolumines- cence properties of the products were investigated.
Uniform ofAgLnMo2O8(Ln=La, Nd, Eu) hierarchical architectures were firstly synthesized via a facile hydrothermal method. These three dimensional architectures were assembled from primary micro-rods and the average diameter was about 5 μm. According to the time-depend experiments, a possible growth mechanism was proposed to be a self-assembling process followed by an Ostwald ripening step. The concentrations of precursor and pH value were also found to have great influences on the final morphologies of the products. In addition, the photolumines- cence properties of the products were investigated.
基金
Supported by the National Natural Science Foundation of China(No.20571025)
the Henan Innovation Project for University Prominent Research Talents,China(No.2005KYCX005)