摘要
采用己二异氰酸酯(HDI)三聚体(HT)合成交联改性聚氨酯水分散体(HPUD),考察了HT添加量对HPUD涂膜的耐水性、耐溶剂性、表干时间、硬度、光泽以及交联度的影响。通过粒径分布仪、热重分析仪(TGA)和傅立叶变换红外光谱仪(FTIR)分别对HPUD乳液贮存过程中粒径的变化、涂膜热稳定性与分子结构进行表征,结果发现,引入质量分数5%~10%的HT可提高聚氨酯涂膜的表干速率和交联度,当w(HT)=10%时,HPUD涂膜具有最佳的综合性能,涂膜表干时间为45min,交联度为80%,吸醇率为78%,吸水率为7%。同时还发现,HPUD涂膜硬度上升速率较快,但最终硬度较未改性聚氨酯水分散体(PUD)有所降低;粒径分析表明,当w(HT)≥20%时,HPUD贮存过程中乳液粒径增大,贮存稳定性下降;TGA分析表明,HPUD涂膜具有较好的热稳定性。
The HDI trimer(HT) modified aqueous polyurethane dispersions(HPUD) were synthesized and the effects of the contents of HT on the water-resistance and solvent-resistance,the degree of crosslinking,hardness,gloss and surface drying time of the HPUD films were discussed.The particle sizes and its distributions,structures and thermal stability of HPUDs and its film were characterized by the dynamic light-scattering technique(DLS),infrared spectra(IR) and thermal gravimetric analysis(TGA),respectively.Results show that introducing 5%~10% of HT into PUD improves the surface drying rate and the crosslinking degree of HPUD films,the HPUD films with 10% HT possess a better performance including 45 min of the surface drying time,80% of the crosslinking degree,78% and 7% of the alcohol-and water-absorption rate.On the other hand,HPUDs display faster film hardness increasing rates and slightly lower final films hardness than those of the common PUDs without HT modification.DLS analysis results show that the particle sizes and its distributions increase and the storage stability decrease with increasing the HT content in the HPUD up to 20% during the storage process.TGA curves indicate that the HPUD films possess a good thermal stability.
出处
《精细化工》
EI
CAS
CSCD
北大核心
2010年第8期755-759,共5页
Fine Chemicals
基金
粤港关键领域重点项目(B10-B2050260)~~
关键词
HDI三聚体
聚氨酯
交联改性
分散体
功能材料
HDI trimer
polyurethane
crosslinking modification
dispersion
functional materials