分析了离心复合高铬铸铁轧辊热处理过程中出现辊身端部裂纹的原因,并制定了改进措施,提高了轧辊的成品率。
The cause of heat treatment crack in high chromium compound centrifugal cast iron milling roll was analyzed.The improvement measure was put forward,the qualified rate of finished product increases.