服役的HK40炉管抗蠕变裂纹扩展能力 被引量:1

Resistance of HK40 furnace tubes against creep crack growth
下载PDF
导出
摘要 在全面分析已服役10年的HK40炉管损伤状况的基础上,研究了HK40炉管母材和焊接接头的蠕变裂纹扩展速率,评价了这2种不同部位抗蠕变裂纹扩展的能力。结果表明在长期正常的运行中,特别是服役后期,下部炉管焊缝中的蠕变裂纹扩展比母材裂纹扩展快。 On the basis of metallographical study of damage states of a HK40 tube which have serviced for ten years, creep crack growth tests on its base metal and weld are carried out, the resistance of the different parts against creep crack growth is studiedThe results show that creep crack growth of the weldments located in the lower part of the furnace tube is faster than that of the base metal after a long period of operation,especially in the later service period Microstructure damage and stress concentration in the weld are two important factors contributing to faster creep crack growth rates
出处 《石油化工设备》 CAS 1999年第3期6-10,共5页 Petro-Chemical Equipment
关键词 炉管 焊缝 蠕变 裂纹扩展 制氢 转化炉 furnace tube, weld, creep crack growth, damage
  • 相关文献

参考文献13

  • 1朱世杰 于永泗 等.蠕变损伤对HK40钢蠕变行为的影响[J].机械工程材料,1988,(4):55-58.
  • 2武川哲也 石丸裕.蒸汽转化炉的历年变化及诸问题[J].化工机械,1979,54(1):43-49.
  • 3笠原晃明.HK40制改质炉管存寿命推定法[J].铁&钢,1979,65(7):975-984.
  • 4吴望周.HK40合金转化炉管焊接接头的失效分析.HK40转化炉管论文集[M].北京:化学工业出版社,1988.24-29.
  • 5王宇林.用C形试样研究HK40炉管蠕变裂纺扩展:硕士学位论文[M].南京:南京化工大学机械学院,1985..
  • 6Tu S D,Int J Pres Ves & Piping,1994年,58卷,3期,345页
  • 7王富岗,石油化工装置失效分析论文选集,1991年,11页
  • 8朱世杰,机械工程材料,1988年,4期,55页
  • 9吴望周,HK40 转化炉管论文集,1988年,24页
  • 10王宇林,硕士学位论文,1985年

共引文献4

同被引文献2

引证文献1

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部