凝固浴对MF-PVA纤维结构与阻燃性能的影响 被引量:3

Effect of Coagulation Bath on Structure and Properties of Melamine Formaldehyde-Polyvinyl Alcohol Fiber
下载PDF
导出
摘要 三聚氰胺甲醛-聚乙烯醇(MF-PVA)纤维是以三聚氰胺、甲醛以及聚乙烯醇水溶液反应制得纺丝原液,采用湿法纺丝制备的MF-PVA纤维。探讨了不同pH值的饱和硫酸钠凝固浴对该纤维的组成变化、形态结构及阻燃性能的影响。氮含量测定及红外光谱分析均证明了MF树脂的溶出量随着凝固浴酸性的增加而增加,造成纤维的表面与横截面粗糙程度越来越大,但极限氧指数(LOI)却越来越高。在酸性一浴法中,凝固浴pH值为3时,其氮流失量高达50%以上,LOI可达37。 Melamine formaldehyde-polyvinyl alcohol (MF-PVA) fiber was ,prepared via wet spinning process, using the blend solution concluded melamine (MA), formaldehyde (F), polyvinyl alcohol (PVA) and water as spinning solution. In this article, we discussed the effects of the saturated sodium sulfate coagulation bath on the composition, morphology, and flame retardant properties of the MF'-PVA fiber by the metods of Kjeldahl method, infrared spectroscopy, scanning electron microscope (SEM) and limiting oxygen index. The results show that both the nitrogen content test and infrared spectrum (IR) prove the quantity of MF resin reduced while the limiting oxygen index (LOI) value of the MF-PVA fiber samples increases as the pH value of coagulation bath decreases. At the same time, the surface and cross-section of the MF-PVA fiber become rougher and rougher appeared in the SEM photos. When the pH value of the coagulation bath is 3, the nitrogen loss and the LOI value of the MF-PVA fiber is respectively 50 % and 37.
出处 《高分子材料科学与工程》 EI CAS CSCD 北大核心 2010年第8期31-34,共4页 Polymer Materials Science & Engineering
基金 国家自然科学基金面上项目(50873061)
关键词 三聚氰胺甲醛-聚乙烯醇纤维 湿法纺丝 凝固浴 结构与性能 melamine formaldehyde-polyvinyl alcohol fiber wet spinning coagulation bath structure and property
  • 相关文献

参考文献5

  • 1YUTAKA N, NOBUO Y. Melamine resin flame-retardant fibers: US, 4088620[P]. 1978-05-09.
  • 2ANIL K, VIMAL K. Modeling and experimental investigation of melamine-formaldehyde polymerization[J]. Macrornolecules, 1990, 23 : 3729-3736.
  • 3JOEY K, DOYLE T K. Water resistant protective garment for fire fighters: US, 6192520[P]. 2001-02-27.
  • 4卢奎林,施楣梧,黄司琪,叶光斗,徐建军.后处理对MF-PVA阻燃纤维结构与性能的影响[J].合成纤维工业,2008,31(1):26-29. 被引量:4
  • 5BERNARD B, SAMUEL A. Melamine and derivatives of melamine [J]. Chem. Rev., 1958, 58(1): 131-172.

二级参考文献5

  • 1董纪震,罗鸿烈,王庆瑞.合成纤维生产工艺学(上册)[M].北京:纺织工业出版社,1994.494-496
  • 2Gupta V B. Heat setting [ J ]. J Appl Polym Sci, 2002,83 ( 3 ) : 586 - 609
  • 3Lee Y M, Kim S H, Kim S J. Preparation and characteristics ofβ- chitin and poly ( vinyl alcohol ) blend [ J ]. Polymer, 1996,37 ( 26 ) :5897 - 5905
  • 4Young No B, Kim M G. Curing of low level melamine-modified urea-formaldehyde particleboard binder resins studied with dynamic mechanical analysis (DMA) [ J ]. Polym Degrad Stab, 2001,74 (1):25-32
  • 5吴温池.应用于高温干态过滤的三聚氰胺纤维滤材的研制[J].产业用纺织品,2000,18(8):19-21. 被引量:5

共引文献3

同被引文献19

引证文献3

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部