高强度多胶粉云母带粘合剂的研制  被引量:9

Preparation of the Binder for Rich Micapaper Tapes with High Strength
下载PDF
导出
摘要 在苯甲酸铅的作用下,将自制的改性剂引入环氧-双马来酰亚胺-TOA体系中,获得了综合性能良好的高强度多胶粉云母带用粘合剂Ia。该粘合剂不仅具有长的室温贮存期(大于四个月),而且其固化体系在维持优良的介电性能的同时,胶条的室温冲击强度为13.6kJ/m~2,155℃的静态弯曲强度为13.0MPa;用玻璃布增强的云母板材,室温冲击强度为81.5kJ/m~2,室温或155℃的静态弯曲强度为283.4MPa或129.IMPa。此外,在温度低于 200℃时,固化物的动态力学模量均大于 100MPa。 The binder Ia for rich micapaper tapes with high strength and other excellent properties is prepared by using a selfmaking modifier introduced into the Epoxy - Bismaleimide - TOA(tung oil anhydride) system with lead benzoate as catalysis. It has long shelf life(more than 4 months) at room temperature due to its high curing reaction apparent activation energy(Ea > 70kJ/mol). The cured system, including bar and mica plank reinforced with glass fiber, remains good dielectricproperties either at room temperature or at 155℃.In addition, for the bar, the impact strength σ_(i) is up to 13. 6 kJ/m^(2) at room temperature, the static flexural strength σ_(f) arrives tol3. 0 MPa at 155℃, and for the mica plank σ_(i) = 81. 5kJ/m^(2),σ_(f) = 283 .4MPa at room temperature and σ_(f) = 129. 1MPa at 155℃. Moreover, within the range from room temperature to 200℃,the dynamic mechanical moduli of binder Ia cured system are greater than 100MPa.
作者 虞鑫海
出处 《中国胶粘剂》 CAS 1999年第2期17-19,29,共4页 China Adhesives
关键词 粉云母带 高强度 胶粘剂 电机 绝缘 binder micapaper tape High strength heat resistant Epoxy - Bismaleimide - tung oil anhydride system
  • 相关文献

参考文献7

  • 1虞鑫海,硕士学位论文,1995年
  • 2金镇镐,张超,潭宇虹,唐传林.云母带用环氧双马来酰亚胺体系粘合剂固化反应的研究[J].哈尔滨电工学院学报,1994,17(3):243-247. 被引量:2
  • 3王国荣,绝缘材料通讯,1983年,5期,67页
  • 4陈复,绝缘材料通讯,1981年,5期,17页
  • 5唐传林,哈尔滨电工学院学报,1978年,2卷,73页
  • 6北京丰盛绝缘材料厂,绝缘材料通讯,1975年,2卷,4页
  • 7桂林电器科学研究所,绝缘材料通讯,1972年,6期,37页

共引文献1

同被引文献81

引证文献9

二级引证文献57

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部