摘要
以聚己二酸-1,4-丁二醇酯(PBA)、甲苯二异氰酸酯(TDI)、二羟甲基丙酸(DMPA)、丙烯酸羟乙酯(HEA)、甲基丙烯酸缩水甘油酯(GMA)为主要原料进行聚合,经三乙胺(TEA)中和,以去离子水乳化后,制得一种稳定的可紫外光固化的新型水性聚氨酯丙烯酸酯乳液。研究了GMA接枝温度和接枝前后的AFM相图,讨论了DMPA用量、总体NCO/OH比值、GMA用量、光引发剂用量对乳液及漆膜性能的影响。
Glycidyl methacrylate （GMA） modified UV -curable waterborne polyurethane emulsion was prepared by using polybutyleneglycol adipate （ PBA2000 ）, toluene diisocyanate （ TDI ）, dimethylolpropionic acid （ DMPA）, 2 - hydroxyethyl acrylate （ HEA）, glycidyl methacrylate （ GMA ） as the main materials. A stable UV - curable waterborne polyurethane emulsion was formed after the neutralization with triethylamine. Effect of the content of GMA, DMPA, NCO/OH ratio and the photoinitiator on performance of WPU emulsion and the films were discussed.
出处
《涂料工业》
CAS
CSCD
北大核心
2010年第9期46-52,57,共8页
Paint & Coatings Industry
关键词
水性聚氨酯
GMA改性
光固化
waterborne polyurethane
modified with GMA
UV - curable