Nanocomposite Ti-Si-N thin films have been deposited on Si （100） substrate by direct current/radio frequency （DC/RF） magnetron sputtering. The effect of varying deposition parameters on the structure and mechanical properties of Ti-Si-N films has been investigated by characterization techniques such as X-ray dif- fraction （XRD）, field emission scanning electron microscopy （FE-SEM）, atomic force microscopy （AFM） and nanoindentation, respectively. XRD analysis of the thin films exhibit all （111）, （200） and （220） peaks initially with varying sputtering pressure, but （111） peak dominates at higher sputtering pressure. The crystallite size calculated from XRD peaks shows that it increases with increasing sputtering pressure. Microstructural analy- sis reveals that the dense blurred grains transform into uniform grains in the films and shows porosity with increasing sputtering pressure. The surface roughness of the Ti-Si-N films increases with varying sputtering pressure. The hardness and Youngrs modulus values of Ti-Si-N films are 33.7 and 278.6 GPa, respectively, with 0.7 Pa sputtering pressure but it decreases with further increase in sputtering pressure due to an increase in porosity of the films.
Nanocomposite Ti-Si-N thin films have been deposited on Si （100） substrate by direct current/radio frequency （DC/RF） magnetron sputtering. The effect of varying deposition parameters on the structure and mechanical properties of Ti-Si-N films has been investigated by characterization techniques such as X-ray dif- fraction （XRD）, field emission scanning electron microscopy （FE-SEM）, atomic force microscopy （AFM） and nanoindentation, respectively. XRD analysis of the thin films exhibit all （111）, （200） and （220） peaks initially with varying sputtering pressure, but （111） peak dominates at higher sputtering pressure. The crystallite size calculated from XRD peaks shows that it increases with increasing sputtering pressure. Microstructural analy- sis reveals that the dense blurred grains transform into uniform grains in the films and shows porosity with increasing sputtering pressure. The surface roughness of the Ti-Si-N films increases with varying sputtering pressure. The hardness and Youngrs modulus values of Ti-Si-N films are 33.7 and 278.6 GPa, respectively, with 0.7 Pa sputtering pressure but it decreases with further increase in sputtering pressure due to an increase in porosity of the films.