Thermo-simulation test and transmission electron microscopy （TEM） have been used to investigate the interaction between the microalloying elements Nb and Mo within the precipitates during relaxation after austenite deformation of C-Ti-Mo steel and C-Nb-Mo steel. The experimental results demonstrated that the austenitic structure was preserved both in C-Ti-Mo steel and C-Nb-Mo steel even if they were relaxed for 1000 s after deformation at 850℃. The strainqnduced precipitate occurs in two kinds of steel. Through the energy spectrum analysis, it was found that the precipitates were Ti（C, N） and Mo-bearing Nb（C, N） respectively and there exists a strong affinity of Mo for Nb with in the precipitates. Mo atoms would enter the lattice of Nb（C, N） particles probably after Nb（C, N） formation.
Thermo-simulation test and transmission electron microscopy （TEM） have been used to investigate the interaction between the microalloying elements Nb and Mo within the precipitates during relaxation after austenite deformation of C-Ti-Mo steel and C-Nb-Mo steel. The experimental results demonstrated that the austenitic structure was preserved both in C-Ti-Mo steel and C-Nb-Mo steel even if they were relaxed for 1000 s after deformation at 850℃. The strainqnduced precipitate occurs in two kinds of steel. Through the energy spectrum analysis, it was found that the precipitates were Ti（C, N） and Mo-bearing Nb（C, N） respectively and there exists a strong affinity of Mo for Nb with in the precipitates. Mo atoms would enter the lattice of Nb（C, N） particles probably after Nb（C, N） formation.
基金
Item Sponsored by Natural Science Foundation of Hebei Province of China (E2008001141)