研究硫化体系对NBR耐油性能和动态性能的影响。结果表明,随着交联密度的增大,采用硫黄硫化体系的NBR硫化胶耐油性能提高,生热降低;与采用普通硫黄硫化体系的NBR硫化胶相比,采用有效硫化体系的NBR硫化胶耐油性能和耐屈挠性能较好,生热较低;采用过氧化物硫化体系的NBR硫化胶在高温(高于70℃)下的耐油性能优于采用硫黄硫化体系的NBR硫化胶;采用过氧化物硫化体系、有效硫化体系和普通硫黄硫化体系的NBR硫化胶玻璃化温度依次升高。
The effect of vulcanization system on oil resistance and dynamic properties of NBR vulcanizates was investigated.The results showed that,as the crosslink density increased,the oil resistance of the NBR cured with sulfur vulcanization system increased,and the heat build-up decreased;compared with conventional vulcanization system,the NBR cured with efficient vulcanization system possessed better oil resistance,better flexing resistance,and lower heat build-up;the NBR cured with peroxide had better oil resistance at high temperature(〉.70 ℃) than the NBR cured with sulfur vulcanization system ;the order of Tg of the NBR cured with 3 different vulcanization systems was as follows:peroxide vulcanization system〈efficient vulcanization system〈conventional vulcanization system.
出处
《橡胶工业》
CAS
北大核心
2010年第9期532-536,共5页
China Rubber Industry
关键词
NBR
硫化体系
耐油性能
动态性能
NBR
vulcanization system
oil resistance
dynamic property