The structure of LiSrY2（BO3）3 has been solved by single-crystal X-ray diffraction analysis at 298 and 113 K on different diffractometers.It crystallizes in trigonal with space group P-3m1（No.164）.The cell parameters at room temperature are as follows：a = 10.3345（9）,c = 6.4049（11） ,V = 592.41（13） 3,Z = 3,Mr = 448.81,F（000） = 618,μ = 21.327 mm-1 and Dc = 3.774 g/cm3.The crystal structure consists of gear-like [BY6O33] groups which are linked together by corner-sharing to form a two-dimensional layer parallel to the ab plane.These layers are connected one after another by sharing oxygen atoms with B（2） atoms along the c direction to construct a three-dimensional framework.Li and Sr atoms just occupy the cavities formed by oxygen atoms.In addition,the vibrational spectroscopy of LiSrY2（BO3）3 and photoluminescence properties of the Eu3＋ doped LiSrY2（BO3）3 were also studied.
The structure of LiSrY2（BO3）3 has been solved by single-crystal X-ray diffraction analysis at 298 and 113 K on different diffractometers.It crystallizes in trigonal with space group P-3m1（No.164）.The cell parameters at room temperature are as follows：a = 10.3345（9）,c = 6.4049（11） ,V = 592.41（13） 3,Z = 3,Mr = 448.81,F（000） = 618,μ = 21.327 mm-1 and Dc = 3.774 g/cm3.The crystal structure consists of gear-like [BY6O33] groups which are linked together by corner-sharing to form a two-dimensional layer parallel to the ab plane.These layers are connected one after another by sharing oxygen atoms with B（2） atoms along the c direction to construct a three-dimensional framework.Li and Sr atoms just occupy the cavities formed by oxygen atoms.In addition,the vibrational spectroscopy of LiSrY2（BO3）3 and photoluminescence properties of the Eu3＋ doped LiSrY2（BO3）3 were also studied.
基金
supported by the Major Research Project of Xi’an University of Arts and Science (No.zd200906)
the Special Fund of Education Committee of Shaanxi Province (No.09JK743)