对G105钻杆管体刺穿部位的观察和试验分析表明,钻杆被刺穿的原因是钻杆在使用前后存放期间保养不当,内壁产生严重的局部腐蚀,形成点蚀坑和产生应力集中点,引起腐蚀疲劳破坏。为提高钻杆的使用寿命,应加强钻杆存放期间的保养和防护。
On the basis of observation and analysis of the through pricks on G105 drill pipes, this article indicates that the occurences of such through pricks are due to improper maintenance of the pipes before and after use. The improper maintenance resnlts in severe pitting corrosion and stress concentration on the inner wall of the pipe and therefrom the corrosion fatigue failure. For the sake of increasing the service life of the pipes, more care should be taken to avoid corrosion on the pipes in storage.