摘要
采用水热法以十二烷基苯磺酸钠为活性剂合成了蓝色纳米荧光GdVO4:Tm粉体。用X射线衍射、扫描电镜、荧光光谱(PL)研究不同反应时间、反应物浓度和Tm3+掺杂量等条件下所得产物的结构和发光性能。结果说明,所得的产物为单一的四方锆型GdVO4:Tm晶体,颗粒大小约为20~50nm;GdVO4:Tm能够被200~320nm的紫外光激发,在278nm波长紫外光激发下发出波长为476nm的明亮蓝光,发光强度分别在反应物浓度为0.205mol/L时、反应时间为3d和Tm3+掺杂量为2%时最高。
GdVO4:Tm blue luminescent nano-powders were prepared via sodium dodecyl benzene sulfonate-assisted hydrothermal technique.The structure and luminescence intensity of the samples at different reaction time,concentration of reacting solution and doped amount of Tm^3+ were characterized by X-ray powder diffraction(XRD),scanning electron microscopy(SEM)and photoluminescence spectroscopy(PL).The experimental results showed that GdVO4:Tm was tetragonal.The production was pure powders with a average diameter from 20 to 50nm.The reaction time,the concentration of reacting solution and doped amount of Tm^3+ were important to the luminescence intensity of the productions.GdVO4:Tm can be excited by 200-320nm ultraviolet radiation.It emits bright blue fluorescence when excited by 278nm ultraviolet radiation.The luminescence intensity of the productions was strongest separately when the concentration of reacting solution was 0.205mol/L,the reaction time was 3d and doped amount of Tm^3+ was 2%.
出处
《功能材料》
EI
CAS
CSCD
北大核心
2010年第A02期210-213,共4页
Journal of Functional Materials
关键词
GdVO4∶Tm
稀土
纳米发光材料
水热
GdVO4:Tm
rare earth
nanocrystalline luminescent materials
hydrotherment