摘要
测定了碱度从２．６到３．４的精炼渣系的炉渣发泡性能，得到了具有较好发泡性能的精炼渣系ＣａＯ５３．２５％，ＳｉＯ２１７．７５％，ＭｇＯ９％，Ａｌ２Ｏ３１５％，ＣａＦ２５％。并通过离差分析方法，得出了炉渣组成对炉渣泡沫化程度的影响顺序为：ＣａＦ２→ＭｇＯ→Ａｌ２Ｏ３→Ｂ（ＣａＯ／ＳｉＯ２）
The foaming ability of refining slag with basicity 2.63.4 was measured, and the refining
slag CaO 53.25%, SiO2 17.75%, MgO 9%, Al2O3 15%, CaF 25% which had batter foaming ability
was obtained. Based on the deviation analysis, the influence sequence of slag ingredient on
foaming index was also obtained as follows: CaF2MgOAl2O3B(CaO/SiO2).
出处
《特殊钢》
北大核心
1999年第3期24-26,共3页
Special Steel