The La-ZSM-5 zeolite with different contents of La was synthesized by the hydrothermal method. The physico-chemical properties of the materials were studied. The results of FT-IR analyses indicated that La might be incorporated into the framework of ZSM-5 zeolite. The NH3-TPD analyses showed that the amount of weak acid sites of the zeolite decreased with a continuously increasing La content. Afterwards, the La-ZSM-5 zeolite was used as the support of PtSnNa catalyst for propane dehydrogenation. The test results revealed that the utilization of La- ZSM-5 zeolite could achieve a high propene conversion, and effectively inhibit the coke formation on the catalyst surface. When the content of La was 0.16%, the catalytic activity and stability of the catalyst got the best of its performance. Besides, the PtSnNa/La （0.16%）-ZSM-5 catalyst is more stable than the conventional PtSnNaLal ZSM-5 catalysts.
基金
the National Nature Science Foundation of China(50873026)
the Science and Technology Support Program of Jiangsu Province (BE2008129)
the"Six Talents Pinnacle Program"of Jiangsu Province(06-A-033) for financial supports