摘要
目的:评价新型眩彩复合体(Twinky Star)的机械性能。方法:通过检测抗压强度(CS)、弯曲强度(FS)、磨耗率(WR)来评价其机械性能。结果:抗压强度结果为252.39±20.82MPa,弯曲强度结果为119.17±18.62MPa,磨耗率测试结果为3.8190±0.61mm3/mm2。结论:新型眩彩复合体(TwinkyStar)具有良好的机械性能,满足口腔临床应用的要求。
Objective：To evaluate the mechanism properties of new Twinky Star compomer.Methods：The samples are prepared and tested with compressive strength test,flexure strength test and wear-resistances test.Results：The compressive strength is 252.39 ±20.82MPa.The flexure strength is 119.17 ±18.62MPa.The wear-resistances result is 3.8190 ± 0.61mm3/mm2.Conclusion：The new Twinky Star compomer possesses good mechanism properties.
出处
《口腔颌面修复学杂志》
2010年第3期172-174,共3页
Chinese Journal of Prosthodontics
关键词
复合体
机械性能
乳牙
compomer
mechanism property
deciduous teeth