Polystyrene/iron-nickel （PS/FeNi3） nanocomposites were synthesized via an in-situ polymerization route and characterized by XRD,SEM and FTIR. FeNi3 nanoparticles were characterized by TEM and XRD. The pure FeNi3 nanoparticles （100～125 nm） were highly clustered and percolated through the PS matrix. When the content of FeNi3 nanoparticles reached 5 wt%,an interaction between FeNi3 nanoparticles and PS matrix was observed. The thermal decomposition behavior of PS/FeNi3 nanocomposites was investigated by thermal analysis. The activation energies （E） and pre-exponential factors （lnA） were calculated by using Archar method. The results show that the thermal decomposition of pure PS is a one-dimensional diffusion mechanism. A three-dimensional diffusion mechanism appears when FeNi3 nanoparticles incorporate. The E of PS/FeNi3 nanocomposites with different FeNi3 contents is 217.5,225.3,180.6 and 73.0 kJ·mol-1,and the corresponding lnA is 35.6,34.9,27.5 and 10.4 S-1,respectively.
Polystyrene/iron-nickel （PS/FeNi3） nanocomposites were synthesized via an in-situ polymerization route and characterized by XRD,SEM and FTIR. FeNi3 nanoparticles were characterized by TEM and XRD. The pure FeNi3 nanoparticles （100～125 nm） were highly clustered and percolated through the PS matrix. When the content of FeNi3 nanoparticles reached 5 wt%,an interaction between FeNi3 nanoparticles and PS matrix was observed. The thermal decomposition behavior of PS/FeNi3 nanocomposites was investigated by thermal analysis. The activation energies （E） and pre-exponential factors （lnA） were calculated by using Archar method. The results show that the thermal decomposition of pure PS is a one-dimensional diffusion mechanism. A three-dimensional diffusion mechanism appears when FeNi3 nanoparticles incorporate. The E of PS/FeNi3 nanocomposites with different FeNi3 contents is 217.5,225.3,180.6 and 73.0 kJ·mol-1,and the corresponding lnA is 35.6,34.9,27.5 and 10.4 S-1,respectively.
基金
supported by the National Natural Foundation of China (No. 10476024)