钼基高温合金表面包埋渗法制备渗铝层的组织与性能 被引量:2

Microstructure and Properties of Aluminized Layers on Mo-Based Superalloy Surface by Pack Cementation Technique
下载PDF
导出
摘要 采用包埋渗法在TZM钼基高温合金表面制备抗氧化的渗铝层,渗铝温度为1 050℃,渗铝时间为12 h;采用SEM、EDS和XRD等分析了渗层的显微组织、物相组成和元素分布等,并对渗层的硬度和抗高温氧化性能进行了研究。结果表明:渗层的相组成为Al_5Mo、Al_3Mo和Al_4Mo;渗层均匀致密,厚度达到130μm,具有双层结构,与基体形成了冶金结合;渗层表面呈颗粒状,其显微硬度达到了8 000 MPa;在800℃×80 h高温氧化下包埋渗铝层具有较好的抗氧化性能。 Oxidation resistant aluminized layers on the TZM Mo-based superalloy surface were prepared by pack cementation technique at 1 050℃for 12 h.The microstructure,phase composition and element distribution of the layers were analyzed by means of SEM,EDS and XRD.The hardness and high temperuture oxidation resistance of the layer were discussed.The results show that the phase composition of the layers were Al_5Mo,Al_3Mo and Al_4Mo.The layer with double layer structure was uniform and compact,whose thichness was 130μm and had a good metallurgical bonding with the substrate.The hardness of the aluminized layer with granular surface was 8 000 MPa. The pack cementation aluminized layer had good oxidation resistance after oxidizing at 800℃for 80 h.
出处 《机械工程材料》 CAS CSCD 北大核心 2010年第9期64-66,93,共4页 Materials For Mechanical Engineering
基金 江苏省科技成果转化专项资金资助项目(BA2007036)
关键词 钼基高温合金 包埋渗 铝化物 高温氧化 Mo-based superalloy pack cementation aluminide high temperature oxidation
  • 相关文献

参考文献10

  • 1吴新光,杜晓斌.TZM合金及其特性[J].中国钼业,2005,29(5):30-31. 被引量:42
  • 2BENZ M G, JACKSON M R, LOU K A, et al. Suppression of carbon monoxide formation in oxide-coated TZM molybde- num X-ray rotating anodes [J]. Journal of Refractory Metals and Hard Materials, 1995,13:327-336.
  • 3PARK J J, BUTT D P, BEARD C A. Review of liquid metal corrosion issues for potential containment materials for liquid lead and lead-bismuth eutectic spallation targets as a neutron source[J]. Nuclear F.ngineering and Deaign, 2000,196: 315-325.
  • 4夏耀勤,王敬生.钼合金搅拌器的制作和应用[J].稀有金属与硬质合金,1997,25(4):48-52. 被引量:4
  • 5SMOLIK G R, PETTI D A, SCHUETZ S T. Oxidation and volatilization of TZM alloy in air[J]. Journal of Nuclear Materials, 2000,283/287 : 1458-1462.
  • 6肖来荣,易丹青,殷磊,李洪武.铌及铌合金高温涂层研究进展[J].材料导报,2004,18(1):13-15. 被引量:21
  • 7XIANG Z D, DATTA P K. Deposition of silicon modified aluminide coatings on nickel base super alloys by pack cementation process[J]. Materials Science and Technology, 2003,19: 935- 942.
  • 8XIANG Z D, ROSE S R, BURNELL-GRAY J S,etal. Co-deposition of aluminide and silieide coatings on γ-TiAl by pack cementation proeess[J]. Journal of Materials Science, 2003,38:19-28.
  • 9MASSALSKI TB. Binary alloy phase diagrams[M]. Ohio: Materials Park, ASM International, 1996.
  • 10CHAKRABORTY S P, BANERJEE S, SINGH K, et al. Studies on the development of protective coating on TZM alloy and its subsequent characterization [J ]. Journal of Materials Processing Technology, 2008,207 : 240-247.

二级参考文献34

  • 1翟金坤,马祥,白新德,侯卫红.C-103铌合金上Si-Cr-Ti料浆熔烧涂层的改性研究[J].航空学报,1994,15(4):499-506. 被引量:20
  • 2冯景苏.铌应用的新进展[J].稀有金属材料与工程,1994,23(3):7-12. 被引量:29
  • 3白林祥,吴维.Pt─Al涂层的高温氧化行为[J].贵金属,1995,16(1):24-29. 被引量:6
  • 4王慧芳,俞淑延.粉末冶金TZM合金板材的性能及其影响因素[J].粉末冶金技术,1990,8(2):75-84. 被引量:7
  • 5Subramanian P R,Mendiratta G M,Dimiduk D M. The development of nb-based advanced intermetallic alloys for structural applications. JOM, 1996 (1) : 33.
  • 6Ro dhammer P, Knabl W, Semprimoschnig C. Protection of Nb-and Ta-Based Alloys Against High Temperature Oxidation. Int J Refractory Metals and Hard Materi 12 (1993-1994):283.
  • 7Kobayashi E,Yoshihara M ,Tanaka R. Improvement in oxidation resistance of the intermetallice compound titanium aluminide by heat treatment under a low partial pressure oxygen atmosphere. High Temperature Technology, 1990,8 (3):179.
  • 8Chou T C. Solid state reactions between MoSi2 and Ir. Ipta Metallurgica et Materialia, 1990(24) : 1131.
  • 9Haasch R T,Tewari S K,Sircar S. Nonequilibrium synthesis of NbA13 and Nb-Al-V alloys by laser cladding:Part Ⅱ oxidation behaviour. Metallurgical transactions A, 1992, 23A(9) : 2631.
  • 10Arata Y, Kobayashi A, Habara Y. Characteristics of gastunnel plasma-sprayed coatings. High Temperature Technology, 1998,6 (1) : 9.

共引文献62

同被引文献58

  • 1申玉田,崔春翔,申玉发,徐艳姬,刘华.Cu-Al合金内氧化的热力学分析——Ⅰ热力学函数[J].稀有金属材料与工程,2004,33(6):576-579. 被引量:9
  • 2涂芳,何柏林.点焊电极强化工艺的研究进展[J].机械工程材料,2005,29(1):23-26. 被引量:9
  • 3陈一胜,魏梅红,段鹏征,刘萍.不同微合金元素对Cu-Cr-Zr组织与性能的影响[J].特种铸造及有色合金,2007,27(5):404-406. 被引量:4
  • 4Shijie Z, Bingjun Z, Zhen Z, et al. Application of lanthanum in high strength and high conductivity copper alloys I-J]. J Rare Earths, 2006,24 (S1) : 385.
  • 5Song K, Xing J, Dong Q, et al. Optimization of the processing parameters during internal oxidation of Cu-A1 alloy powders using an artificial neural network[J]. Mater Des, 2005,26(4) :337.
  • 6Yasar I, Canakci A, Arslan F. The effect of brush spring pressure on the wear behaviour of copper-graphite brushes with 'electrical current[J]. Tribology Int, 2007,40(9) : 1381.
  • 7Siegert K, Huber S. Forming of spray formed copper alloys with injected carbon[J]. Mater Sci Eng A, 2002,326(1) : 63.
  • 8Li Z, Shen J, Cao F, et al. A high strength and high con- ductivity copper alloy prepared by spray forming[J]. J Mater Process Techn, 2003,137 (1-3) : 60.
  • 9Jordan N, Schroder R, Harig H, et al. Influences of the spray deposition process on the properties of copper and copper alloys[J]. Mater Sci Eng A,2002,326(1):51.
  • 10Annavarapu S, Doherty R D. Evolution of microstructure in spray easting[J]. Int J Powder Metall, 1993,29(4) : 331.

引证文献2

二级引证文献34

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部