Hypereutectic Al-17.5Si （wt pct） and Al-25Si （wt pct） alloys with various content of rare earth Er were prepared by conventional casting technique. The effect of Er on the microstructure and properties of the hypereutectic Al-Si alloys was investigated using optical microscopy, scanning electron microscopy as well as friction and wear tests. It was found that optimal amount of Er exists in modifying the hypereutectic Al-Si alloys. An appropriate addition of Er improved the anti-wear properties, and reduced the friction coefficient of the hypereutectic Al-Si alloys studied. The primary silicon crystals in the hypereutectic Al-Si alloys were refined with the suitable addition of Er element. The modification mechanism was also discussed in this paper.
Hypereutectic Al-17.5Si （wt pct） and Al-25Si （wt pct） alloys with various content of rare earth Er were prepared by conventional casting technique. The effect of Er on the microstructure and properties of the hypereutectic Al-Si alloys was investigated using optical microscopy, scanning electron microscopy as well as friction and wear tests. It was found that optimal amount of Er exists in modifying the hypereutectic Al-Si alloys. An appropriate addition of Er improved the anti-wear properties, and reduced the friction coefficient of the hypereutectic Al-Si alloys studied. The primary silicon crystals in the hypereutectic Al-Si alloys were refined with the suitable addition of Er element. The modification mechanism was also discussed in this paper.
基金
supported by the National Key Technology R&D Program of China(No.2009BAE80B00)