温度梯度对定向凝固TiAl基合金片层取向的影响 被引量:7

EFFECTS OF TEMPERATURE GRADIENT ON LAMELLAR ORIENTATIONS OF DIRECTIONAL SOLIDIFIED TiAl-BASED ALLOY
原文传递
导出
摘要 利用定向凝固方法研究了在1580和1650℃加热温度下Ti-47Al-2Cr-2Nb合金不同片层取向的晶粒竞争生长规律.显微组织分析表明,合金初生相为β相,随后发生包晶反应形成α相,并在β→α转变时α相依附已有β相形核,12种α变体中仅形成了一种特定取向的α变体,两相区平均温度梯度由40K/cm增大至160K/cm,从而使凝固界面形态由柱状树枝晶转变为胞状树枝晶.在排除切割面影响的前提下,对γ片层取向的演变过程进行了分析.结果表明,在1mm/min的抽拉速度下,温度梯度为40K/cm(加热温度为1580℃)时,与生长方向呈74°左右的柱状晶逐渐淘汰其他与生长方向约呈45°的晶粒;提高温度梯度至160K/cm(加热温度为1650℃)时,与生长方向呈74°左右的柱状晶逐步淘汰其他与生长方向约呈90°的晶粒而生长占优.晶体取向计算表明,在本实验条件下β枝晶倾向于沿〈110〉_β方向择优生长,提高温度梯度使β枝晶沿〈110〉_β方向择优生长趋势增强,〈001〉_β等其他取向枝晶被更快淘汰. Directional solidification experiments under heating temperatures of 1580℃and 1650℃were performed on Ti-47Al-2Cr-2Nb alloy in order to obtain the evolution of lamellar grains.Prom microstructural analysis in the mushy zone of directional solidified ingots,βphase was firstly solidified, thenαphase was formed through peritectic reaction;αphase depended on the pre-existedβphase on which it nucleated,and only one of the 12αorientation variants was selected during solid stateβ→αtransformations.As the average temperature gradient of the mushy zone was increased from 40 K/cm to 160 K/cm,the solidification interface morphologies were changed from columnar dendrite to celluar dendrite.Eliminating the influence of cutting plane to theγ-lamella orientation,it was shown that the columnar lamellar grains with an angle of approximately 74°to growth direction gradually overgrew the ones with the angle of nearly 45°to the growth direction at the withdrawal rate of 1 mm/min and temperature gradient of 40 K/cm.Increasing temperature gradient to 160 K/cm,the grains with the angle of about 74°progressively rejected other with the angle of nearly 90°to the growth direction.Calculation of theβdendrite preferred growth orientation indicated thatβdendrites tend to grow along the 110βorientation at the present solidification experiments.Increasing temperature gradient,the preferred growth tendency ofβdendrite became more drastically,other orientations,such as the 001βdirectional orientation,could rapidly be replaced.
出处 《金属学报》 SCIE EI CAS CSCD 北大核心 2010年第10期1223-1229,共7页 Acta Metallurgica Sinica
关键词 TIAL基合金 定向凝固 片层取向 择优生长 TiAl-based alloy directional solidification lamellar orientation preferred growth
  • 相关文献

参考文献20

  • 1Yamaguchi M, Inui H, Ito K. Acta Mater, 2000; 48:307.
  • 2Dimiduk D M. Mater Sci Eng, 1999; A263:281.
  • 3Kim Y W. JOM, 1995; 47:39.
  • 4Yamaguchi M, Johnson D R, Lee H N, Inui H. Intermetallics, 2000; 8:511.
  • 5Kishida K, Johnson D R, Masuda Y, Umeda H, Inui H, Yamaguchi M. Intermetallics, 1998; 6:679.
  • 6Johnson D R, Inui H, Muto S, Omiya Y, Yamanaka T. Acta Mater, 2006; 54:1077.
  • 7Lee H N, Johnson D R, Inui H, Oh M H, Wee D M, Yamaguchi M. Mater Sci Eng, 2002; A329-331:19.
  • 8Takeyama M, Yamamoto Y, Morishima H, Koike K, Chang S Y, Matsuo T. Mater Sei Eng, 2002; A329 331:7.
  • 9Lee H N, Johnson D R, Inui H, Oh M H, Wee D M, Yamaguchi M. Acta Mater, 2000; 48:3221.
  • 10Jung I S, Oh M H, Park N J, Kumar K S, Wee D M. Met Mater Int, 2007; 13:455.

二级参考文献3

  • 1蒋成保,博士学位论文,1996年
  • 2安阁英,金属科学与工艺,1985年,14卷,55页
  • 3蒋成保,Acta Metall Mater

共引文献11

同被引文献52

引证文献7

二级引证文献15

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部