某环氧钢筋涂料防腐蚀性能研究

Anti-corrosion Performance of an Epoxy Rebar Paint
下载PDF
导出
摘要 在海洋环境和使用融雪剂的地方,由氯离子渗透所引起的混凝土内钢筋锈蚀是导致钢筋混凝土结构失效的主要原因。研制了一种用于混凝土内钢筋表面的溶剂型环氧防腐蚀涂料体系。研究了防锈颜料、玻璃鳞片的种类、用量等对底漆和面漆防腐蚀性能的影响。结果表明,选用云母氧化铁和三聚磷酸铝作为底漆防锈颜料,颜料体积浓度(PVC)控制在25%-31%之间,面漆添加27%左右经偶联剂处理后的120目左右玻璃磷片,可获得抗氯离子渗透能力较好的涂层。 At marine environments and the places using snow-melting agents,the rebar corrosion caused by penetration of chloridion is a major factor which can lead to invalidation of concrete structures.A solvent based anti-corrosion paint system applied to rebar surface of concrete structure had been developed.The influences of anti-corrosion pigments and glass flakes on anti-corrosion performance of the primer and top coating were studied.The results showed that the coating system with 25% ~ 31% micaceous ferric oxide and mel-phosphate aluminium as anti-corrosion pigments of primer and with an addition of 27% glass flakes treated by coupling agent to the top coating had good resistance to chloridion penetration.
出处 《腐蚀与防护》 CAS 北大核心 2010年第10期763-768,共6页 Corrosion & Protection
关键词 涂料 钢筋 防腐蚀 防锈颜料 玻璃鳞片 paint rebar anti-corrosion anti-rust pigment glass flake
  • 相关文献

参考文献5

  • 1吴希革.一种钢筋重防腐耐划粉末涂料[P].CN1687269,2005-10-26.
  • 2周思岳.厚涂层钢绞线专用环氧粉末涂料及其制备方法[P].CN1962779,2007-05-16.
  • 3孙立为.混凝土中钢筋防腐专用水性漆[P].CN101397476,2009-04-01.
  • 4王晓东,侯锐钢.玻璃鳞片涂料的应用[J].热固性树脂,2005,20(1):47-49. 被引量:7
  • 5JG3042-1997.环氧树脂涂层钢筋(附录C)[s].

二级参考文献6

  • 1中国腐蚀与防护学会.腐蚀与防护全书[M],合成树脂及玻璃钢[M].化学工业出版社,1989..
  • 2竹村.玻璃鳞片树脂衬里技术[D].上海:中日耐蚀高分子材料国际交流会,1994..
  • 3三浅克弘.玻璃鳞片增强的乙烯基酯树脂衬里的特点和应用[C].上海:中日耐蚀高分子材料国际交流会,1994..
  • 4奥田聪.耐蚀塑料的技术发展动态[Z].,1994..
  • 5S Okuda, M Takada. Society of chemical engineers, Japan, Annum Meeting, 1993.
  • 6陆士平,胡剑斌.耐蚀鳞片胶泥在脱硫烟道中的应用[J].中国环保产业,2000(3):26-27. 被引量:5

共引文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部