工艺参数对热浸镀锌抑制层的影响 被引量：1

Effect of Processing Parameters on Inhibition Layer During Hot Dip Galvanizing
下载PDF
导出
摘要 从锌液中Al含量、带钢入锅温度、锌液流动性和浸镀时间四个方面阐述了热浸镀锌过程中工艺参数对抑制层的影响,为在热浸镀过程中得到较好的抑制层,进而得到优质的镀层产品提供了理论依据。 The effects of Al content in zinc bath,strip temperature,flow rate of zinc bath and dipping time on inhibition layer during hot dip galvanizing are reviewed.The analyses of the four processing parameters may provide theory basis for producing high quality galvanized sheets.
作者 陈斌锴 郝晓东 袁训华 江社明 李远鹏 张启富
机构地区 钢铁研究总院
出处 《腐蚀与防护》 CAS 北大核心 2010年第10期790-793,共4页 Corrosion & Protection
关键词 热浸镀锌 工艺参数 抑制层 hot dip galvanizing processing parameter inhibition layer
分类号 TG174.44 [金属学及工艺—金属表面处理]
  • 相关文献

参考文献10

  • 1Chen H B, Yang K C, Hsieh C K, et al. Effect of galvanizing parameters on the microstructure of hot-dip galvanized steel sheet for aulomobotive panals[C]// Galvatech'07,2007 : 297 -302.
  • 2Monojit Dutta, Shiv Brat Singh. Effect of temperature on the formation of an Fe2 Ais inhibition layer during hot-dip galvanizing [J]. Scripta Materialia, 2009, 60: 643-646.
  • 3Guttmann M, Lepretre Y, Aubry A. Mechanisms of the galvanizing reaction. Influence of Ti and P contents in steel and its surface microstructure after annealing [C]//The Iron and Steel Society, 1995.. 295--307.
  • 4Komatsu A, Uchida Y, Andoh A, et al. Changing process from ξ center dot Fe-Zn phase to A1-Fe intermetallic compounds in molten Zn-5 mass% Al alloy bath[C]//GALVATECH'98,1998 : 127- 132.
  • 5McDevitt E T, Morimoto Y, Meshii M. Microstructural evolution during galvannealing, Part II: Formation and growth of the Fe-Zn intermetallic compounds [C]//GALVATECH'98,1998:161 -- 167.
  • 6卢锦堂,许乔瑜,孔纲.热浸镀技术与应用[M].北京:机械工业出版社,2007:49-54.
  • 7Chen Lihua, Richard Fourmentin, Joseph McDermid. Short term formation of the inhibition layer during continuous hot-dip galvanizing [ C]//Galvatech' 07, 2007: 321- 326.
  • 8Doojin Paik, Moonhi Hong, Yeongsool Jin. The optimization of the inhibition layer to obtain compact surfaces of the galvannealed steel sheets during galvannealing processes [C]//Galvatech' 04, 2004 : 481 -- 490.
  • 9Doo-Jin Paik, Myung-Soo Kim, Chang-Woon Jee, et al. Reactions of the steel substrates in a molten zinc bath to form an inhibition layer at the interface and precipitation of the dross particles during galvannealing process[C]//Galvatech'07,2007:315 - 320.
  • 10Lin C S,Meshi M,Cheng C C, et al. Phase evolution galvanneal coating on sheet steel[J]. ISU. 1995, 35 (5) :503--511.

共引文献4

同被引文献7

引证文献1

二级引证文献10

腐蚀与防护
2010年 第10期

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部