摘要
在不同温度梯度及生长速度下测量了Al-Al3Ni共晶合金间距选择范围实验结果表明,在一定生长速度下,共晶间距存在一容许范围,其宽度随生长速度的增加而减小在某一温度梯度下,共晶间距与生长速度的关系满足常数(n=1.7-2.0)的关系.温度梯度增加,其最大、最小及平均间距略有减小同时。
In order to establish eutectic spacing selection criterion for directionally solidified eutecticalloys, Al-Al3Ni interrod spacings were studied at different thermal gradients and growth velocities. It is shown that a sharp distribution of spacing is observed for a given velocity. The width of the distributionis found to decrease as the velocity is increased. The relationship between the spacing and pulling velocityfor a given thermal gradient can be expressed as v = constant when n is from 1.7 to 2.0. The maximum,minimum and average spacings will be slightly decreased while thermal gradient increases. Meanwhile,a number of velocity change experiments was also carried out and it is shown that spacing selection inAl-Al3Ni alloy is independent of the initial growth velocity for a given final velocity.
出处
《金属学报》
SCIE
EI
CAS
CSCD
北大核心
1999年第4期353-356,共4页
Acta Metallurgica Sinica
关键词
间距
控制参数
Al-Al3Ni
共晶合金
spacing selection, controlling parameter, Al-Al3Ni eutectic alloy