根据迁钢公司板坯铸机生产中碳高锰钢的生产实践调查影响纵裂的因素,分析了纵裂发生的原因,通过采取一定的措施,使得中碳高锰钢的纵裂得到了控制。
The factor causing longitudinal cracks were investigated by analyzing the data of medium-carbon high-manganese steel.The reason of longitudinal cracking of slab was analyzed.Some measures were taken to decrease the longitudinal crack defects on the slab of medium-carbon high-manganese steel.