摘要
构建了氧电极材料分别为(La,Sr)MnO3/YSZ(LSM/YSZ)和La0.6Sr0.4Co0.2Fe0.8O3-δ(LSCF)的固体氧化物电解池(SOEC)。在750℃、电流密度为0.25A/cm2的SOEC模式下,分别对两种类型的SOEC进行了约110h的电解实验。结果表明,LSM/YSZ可能是较好的SOEC氧电极材料。依据电化学表现、XRD和微观结构,阐述了两种类型SOEC氧电极性能表现的可能机理。
Two planar solid oxide electrolysis cells (SOEC) are fabricated using (La, Sr)MnO3/YSZ( LSM/ YSZ) and La0. 6 Sr0. 4 Co0. 2 Fe0. 8 O3-δ (LSCF) for oxygen electrodes, respectively-. Two-types SOEC are operated on elec- trolysis tests at 750℃ with a current density of 0. 25A/cme for 110 hours. It indicates that LSM/YSZ may be a good candidate for oxygen electrode of SOEC. In terms of the electrochemical characterization, X-ray diffraction and micro structural characterization for LSM/YSZ and LSCF oxygen electrodes, possible mechanisms of the oxygen reduction and evolution reaction fOr two-type oxygen electrodes are proposed.