摘要
合成了两种分子主链结构上含有氨基和酰亚胺结构的自催化氰基单体,采用1H-NMR对单体结构进行了表征,运用DSC对其固化行为进行研究,并与其他可自催化氰基单体进行对比,运用FTIR和TGA对固化物的结构和热稳定性进行了初步表征。DSC测试结果表明,含酰亚胺结构的自催化氰基单体熔融后,250~300℃给出明显的固化放热峰。FTIR验证了氰基固化形成的结构。TGA测试表明其具有较好的热性能,空气和N2中的Td5均高于510℃,且N2中残重高于60%。
Two kinds of self-catalyst cyano resin with NH2-group and imide structure in the main chain were synthesized, whose struture were characterized with 1H-NMR. DSC was used to investigate the curing behavior of the cyano resin and comparison was made with other self-catalyst monomer. The structure and thermal properties of cured resin were studied with FTIR and TGA respectively. The results of DSC show that both of the self-catalyst cyano resins give on exothermic peak from 250 to 300℃ after melting, due to the curing reaction. Furthermore, FTIR spectra demonstrated that the expected structures of cured resins are formed. And the resins have excellent thermal property, Td^5 of which is above 510℃ not only in nitrogen but also in air, the decomposition residues of which is over 60% in nitrogen at 900℃.
出处
《宇航材料工艺》
CAS
CSCD
北大核心
2010年第2期45-48,共4页
Aerospace Materials & Technology
关键词
氰基树脂
耐高温
酰亚胺
自催化
Cyano group resin
High-temperature resistent
Imide structure
Selt-catalyst