An ultrafine grained Fe-40Al intermetallic compound is fabricated by a self- propagating high temperature synthesis （SHS） casting. The XRD result shows that the Fe-40Al intermetallic compound consists of the B2 FeAl phase. The Fe-40Al intermetallic compound presents ultrafine grain size in the range of 100-600 rim, leading from the high nucleation rate and the low growth rate. The Fe-40Al intermetallic compound exhibits high hardness （3.4 GPa） and high bending strength （830 MPa） and high compressive strength （2700 MPa）, which originate from the ultrafine-structure in the material. The effect of the load on dry-sliding wear rate of the material against AISI52100 steel was investigated. The wear rate increases with the increase of normal load. The dominated weax mechanism is microfracture.
An ultrafine grained Fe-40Al intermetallic compound is fabricated by a self- propagating high temperature synthesis （SHS） casting. The XRD result shows that the Fe-40Al intermetallic compound consists of the B2 FeAl phase. The Fe-40Al intermetallic compound presents ultrafine grain size in the range of 100-600 rim, leading from the high nucleation rate and the low growth rate. The Fe-40Al intermetallic compound exhibits high hardness （3.4 GPa） and high bending strength （830 MPa） and high compressive strength （2700 MPa）, which originate from the ultrafine-structure in the material. The effect of the load on dry-sliding wear rate of the material against AISI52100 steel was investigated. The wear rate increases with the increase of normal load. The dominated weax mechanism is microfracture.
基金
supported by the National Natural Science Foundation of China (No50801064)
the National Basic Research Program of China(No2007CB607601)