The microstructure of experimental nickel-base single crystal superalloys with different levels of carbon has been studied. The results indicated that with increasing carbon addition, the liquidus temperature decreased obviously and the as-cast microstructures exhibited a decrease in the amount of γ/γ′ eutectic structure and an increase in the volume fraction of carbides. The carbides formed in these alloys were most script-type MC carbides which appeared continuous dendritic networks in the interdendritic region. The segregation behavior of element W was influenced by the carbon addition.
The microstructure of experimental nickel-base single crystal superalloys with different levels of carbon has been studied. The results indicated that with increasing carbon addition, the liquidus temperature decreased obviously and the as-cast microstructures exhibited a decrease in the amount of γ/γ′ eutectic structure and an increase in the volume fraction of carbides. The carbides formed in these alloys were most script-type MC carbides which appeared continuous dendritic networks in the interdendritic region. The segregation behavior of element W was influenced by the carbon addition.
基金
supported financially by the National Natural Science Foundation of China (Grant No. 50771081,50931004)
the National Basic Research Program of China (2010CB631202)