摘要
运用高温磁测系统对航空航天及通信用永磁材料在28~160℃高温范围进行了高温Q点稳定性试验研究。结果表明,在28~160℃范围内,随着温度的升高,铝镍钴永磁合金的磁能积、剩磁和矫顽力都有所下降的同时,LNGT32剩磁损失(a=hT(℃))大于LNGT64的剩磁损失(a=hT(℃)),而LNGT32高温Q点(tanθ=Bd/Hd)的稳定性小于LNGT64永磁材料的高温Q点(tanθ=Bd/Hd)的稳定性。
The magnetic performance of two AlNiCo hard magnet alloys used in aero field was measured by high temperature magnetic testing system AMT-4 between 28-160℃. Results show that with the increase of temperature the performance of AlNiCo alloys decreases. LNGT32 alloy has a larger magnetism loss(a=hT(℃))than LNGT64 between 28-160℃, while LNGT64 alloy has a more stable Q workstation(tanθ=Bd/Hd) than LNGT32 alloy.