摘要
The electrochemical process of galena in a pH 12.8 buffer solution was investigated using chronoamperometry and chronopotentiometry. To establish kinetic parameters on the surface of galena in the diethyldithiocarbamate solution, the exchange current density and the dependence of current density on reaction time were determined. Experimental results demonstrate that the exchange current density of galena is 1.585× 10^-2A/m2 in the diethyldithiocarbamate-free solution. In the diethyldithiocarbamate solution, the thickness of lead diethyldi- thiocarbamate adsorbed on the surface of galena is 3.28 molecular layers, the diffusion coefficient of diethyldithiocarbamate on the surface of galena electrodes is 1.13 × 10^-10 m2/s, and the exchange current density of galena is 0.45 A/m2. Lead diethyldithiocarbamate on the surface of galena is firmly adsorbed.
The electrochemical process of galena in a pH 12.8 buffer solution was investigated using chronoamperometry and chronopotentiometry. To establish kinetic parameters on the surface of galena in the diethyldithiocarbamate solution, the exchange current density and the dependence of current density on reaction time were determined. Experimental results demonstrate that the exchange current density of galena is 1.585× 10^-2A/m2 in the diethyldithiocarbamate-free solution. In the diethyldithiocarbamate solution, the thickness of lead diethyldi- thiocarbamate adsorbed on the surface of galena is 3.28 molecular layers, the diffusion coefficient of diethyldithiocarbamate on the surface of galena electrodes is 1.13 × 10^-10 m2/s, and the exchange current density of galena is 0.45 A/m2. Lead diethyldithiocarbamate on the surface of galena is firmly adsorbed.
基金
supported by the National Nature Science Foundation of China (No.50704018)
the Natural Science Foundation of Jiangxi Province, China (No.2007GQC0643)