The effects of surface conditioning methods on the microtensile bond strength of Y-TZP ceramic were studied based on airborne particle abrasion and resin cements.Eight square-shaped（φ12 mm×5 mm high） Y-TZP ceramic were studied blocks（LAVATM,3M ESPE,USA） and flat occlusal dentin blocks were fabricated,pre-treated（airborne abrasion with 125μm Al2O3 particles,tribochemical silica coating with 110 μm Al2O3 particles modified by silica oxide）,and bonded to each other using resin cements（Panavia F 2.0,RelyX Unicem）.Thereafter the trilayer specimens were cut into microbar specimens with a bonding area of approximately 1.0±0.1 mm2 and then microtensile bond strength tests were performed.The Y-TZP ceramic following airborne particle abrasion with 125μm Al2O3 and silicoating,the surface roughness of Y-TZP and its surface silica content were confirmed to increase.Overall,the Y-TZP ceramic surface treatment with a tribochemical silica coating showed the highest microtensile bond strength of the phosphate monomer-based resin cement to Y-TZP ceramic（mean MPa=18.11±0.27（Panavia F 2.0）,17.45±0.39（Rely X Unicem）.In cases in which a silica coating was applied,there was no significant difference in the bonding strength depending on resin cements（P0.05）.
The effects of surface conditioning methods on the microtensile bond strength of Y-TZP ceramic were studied based on airborne particle abrasion and resin cements.Eight square-shaped（φ12 mm×5 mm high） Y-TZP ceramic were studied blocks（LAVATM,3M ESPE,USA） and flat occlusal dentin blocks were fabricated,pre-treated（airborne abrasion with 125μm Al2O3 particles,tribochemical silica coating with 110 μm Al2O3 particles modified by silica oxide）,and bonded to each other using resin cements（Panavia F 2.0,RelyX Unicem）.Thereafter the trilayer specimens were cut into microbar specimens with a bonding area of approximately 1.0±0.1 mm2 and then microtensile bond strength tests were performed.The Y-TZP ceramic following airborne particle abrasion with 125μm Al2O3 and silicoating,the surface roughness of Y-TZP and its surface silica content were confirmed to increase.Overall,the Y-TZP ceramic surface treatment with a tribochemical silica coating showed the highest microtensile bond strength of the phosphate monomer-based resin cement to Y-TZP ceramic（mean MPa=18.11±0.27（Panavia F 2.0）,17.45±0.39（Rely X Unicem）.In cases in which a silica coating was applied,there was no significant difference in the bonding strength depending on resin cements（P0.05）.