摘要
通过生产出口铸钢件的工艺实践，针对铸件出现的裂纹、缩裂等铸造缺陷，摸索出一套比较行之有效的工艺措施。提出用高温力学的思路来分析裂纹、缩裂产生的原因。
AbstractEffective
technology implementation has been found out during practice in production of exported steel
castings by aiming at occurring of crack and shrink of castings.High temperature mechanics has
been used to analyse causes of such defects hence effective way to avoid from casting defects.
出处
《中国铸造装备与技术》
CAS
1999年第4期32-34,共3页
China Foundry Machinery & Technology