Nb-B复合高强度集装箱用钢的高温变形行为 被引量:4

HOT DEFORMATION BEHAVIOR OF A HIGH STRENGTH CONTAINER STEEL COMPOUNDED WITH Nb-B
原文传递
导出
摘要 在Gleeble-1500热模拟试验机上,通过单道次高温压缩变形实验,研究Nb-B复合高强度集装箱用钢的高温变形行为.结果表明:在本实验所采用的变形工艺参数范围内,实验钢在热加工硬化过程中,当应变速率为0.1和1 s^(-1)时,应变硬化指数n与真应变ε曲线上出现"单波峰"和"单波谷";应变速率为5和15 s^(-1)时,应变硬化指数n与真应变ε曲线上出现"双波峰"和"双波谷"现象,在热加工硬化过程中的硬化机制以位错强化、孪晶强化和析出强化为主.根据Zener-Hollomon和Ludwik方程,对实验数据进行非线性拟合,得出在1123—1423 K范围内的变形激活能和应力指数分别为(428.188±20.109)kJ/mol和4.923,并建立了Z参数的表达式、热变形方程、动态再结晶的模型图. Hot deformation behaviors of high strength container steel compounded with Nb-B have been systematically studied through high temperature compression tests on the Gleeble-1500 thermal-mechanical simulator. In the present deformation conditions, there are different relationships between the strain hardening exponent (n) and the true strain (ε) under different strain rates at the deformation temperature of 1423 K; n-εcurves have single peak and single valley at the strain rates of 0.1 s^-1 and 1s^-1, while n-εcurves have double peaks and double valleys at the strain rates of 5 s^-1 and 15 s^-1.During the heat work-hardening process, dislocation strengthening, twin strengthening and precipitation strengthening are the major work-hardening mechanisms of the tested steel. According to Zener-Hollomon and Ludwik equation, the experimental data have been regressed by using nonlinear method, the apparent deformation activation energy (Q) and stress exponent (n) were obtained to be about (428.188±20.109) kJ/mol and 4.923 in the temperature range of 1123 K—1423 K, respectively. Finally, an expression of Z parameter, hot deformation equation and dynamic recrystallization model diagram of the tested steel are established.
出处 《金属学报》 SCIE EI CAS CSCD 北大核心 2011年第1期34-40,共7页 Acta Metallurgica Sinica
关键词 Nb-B钢 真应力-真应变曲线 应变硬化指数 动态再结晶 激活能 Nb-B steel true stress-true strain curve strain hardening exponent dynamic recrystallization activation energy
  • 相关文献

参考文献2

二级参考文献13

  • 1王松涛,杨柯,单以银,李来风.高氮奥氏体不锈钢与316L不锈钢的冷变形行为研究[J].金属学报,2007,43(2):171-176. 被引量:33
  • 2ASM,马九荣,陈立敏译.金属手册.北京:机械工业出版社,1994:7.
  • 3Soussan A, Degallaix S. Mater Sci Eng, 1991; A142:169.
  • 4Ludwigson D C, Berger J A. JISI, 1969; 207:63.
  • 5Simmons J W. Acta Mater, 1997; 45:2467.
  • 6Lan S H, Lee H J, Lee S H. Mater Des, 2009; 30:3881.
  • 7Jha B K, Ram A, Sagar D V. J Mater Sci Lett, 1987; 6: 891.
  • 8Mejia I, Maldonado C, Benito J A. Mater Sci Forum, 2006; 509:37.
  • 9Remy L. Metall Trans, 1981; 12A: 387.
  • 10Karaman I, Sehitoglu H, Maier H J. Acta Mater, 2001; 49: 3919.

共引文献50

同被引文献43

  • 1尚成嘉,杨善武,王学敏,侯华兴,于功利,王文仲.低碳贝氏体钢的组织类型及其对性能的影响[J].钢铁,2005,40(4):57-61. 被引量:70
  • 2陈庆军,康永林,苏世怀,张建平,骆小刚.微合金高强度耐候钢的试验研究[J].钢铁,2005,40(7):60-63. 被引量:14
  • 3曹金荣,刘正东,程世长,杨钢,谢建新.应变速率和变形温度对T122耐热钢流变应力和临界动态再结晶行为的影响[J].金属学报,2007,43(1):35-40. 被引量:47
  • 4贺信莱,尚成嘉,杨善武等.高性能低碳贝氏体钢[M].北京:冶金工业出版社,2008.
  • 5文新理.700MPa级薄规格集装箱板成分设计和组织性能控制[D].北京.北京科技大学,2010:8.
  • 6SUCHIRO M, LIU Z K, AGREN J. Effect of Niobium on massive transformation in ultra low carbon steels, a solute drag treatment [ J ]. Acta Mastee, 1995, 44: 4241 - 4244.
  • 7PRASAD S N, MEDIRATFA S R, SARMA D S. lnilu- ence of austeniitisation temperature on the structure and properties of weather resistant steel [ J ]. Mater Sci Eng, 2003, A385:288 - 297.
  • 8ZHAO Y T, YANG S W, SHANG C J, et al. The me- chanical properties and corrosion behavior of ultra-low carbon microalloying steel [ J ]. Materials Science and Engineering, 2007, 454 - 455 (25): 695 - 700.
  • 9ZHAO Y T, YANG S W, GUO H, et al. Rust layer structure and corrosion resistance of high strength mi- croalloyed Steels[ J ]. Materials Science forum, 2007, 539 - 543 : 4774 -4779.
  • 10YAMASHITA M, KONISHI H, MIZUKI J, et al. Nano-strueture of protective rust layer on weathering steel exposed in nation-wide enviromnents in Japan [ C]//First International Conterence on Advanced Structural Steels, Tsukuba: The Iron and Steel Institute of Japan, 2002 : 287 - 288.

引证文献4

二级引证文献13

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部