摘要
用电弧炉熔炼法制备了Pr0.1Ce0.6Tb0.3Fe1.9-xBx（x=0.00-0.20）合金。分别采用X射线衍射（XRD）、振动样品磁强计（VSM）和应变仪分析了合金的结构、居里温度和磁致伸缩。研究发现,所有样品均呈现单一MgCu2型Laves相结构;随B含量的增加,晶格常数在x≤0.1时缓慢下降而在x〉0.1时快速下降;居里温度在x=0.1处出现峰值;B的引入导致了合金室温磁致伸缩性能的下降。
Pr0.1Ce0.6Tb0.3Fe0.9 xBx alloys （x=0-0.20） were fabricated by arc-melting method. The structure, Curie temperature and magnetostriction of the alloys were investigated by means of X-ray diffraction, vibrating sample magnetometer and standard strain technique. All the samples present MgCu2-type Laves phase structure. The lattice parameter decreases slightly with x when x≤0.1, and decreases rapidly when x〉0.1 with increasing B content. Curie temperature exhibits a maximum value at x=0.1. The magnetostriction at room temperature decreases due to the addition of boron.